Influence of Single-Wall Carbon Nanotube Suspension on the Mechanical Properties of Polymeric Films and Electrospun Scaffolds.

Carbon nanotubes (CNTs) are used in applications ranging from electrical engineering to medical device manufacturing. It is well known that the addition of nanotubes can influence the mechanical properties of various industrial materials, including plastics. Electrospinning is a popular method for fabricating nanomaterials, widely suggested for polymer scaffold manufacturing. In this study, we aimed to describe the influence of single-walled carbon nanotube (SWCNT) suspensions on polymeric poured films and electrospun scaffolds and to investigate their structural and mechanical properties obtained from various compositions. To obtain films and electrospun scaffolds of 8 mm diameter, we used poly-ε-caprolactone (PCL) and poly(cyclohexene carbonate) (PCHC) solutions containing several mass fractions of SWCNT. The samples were characterized using tensile tests, atomic force and scanning electronic microscopy (AFM and SEM). All the studied SWCNT concentrations were shown to decrease the extensibility and strength of electrospun scaffolds, so SWCNT use was considered unsuitable for this technique. The 0.01% mass fraction of SWCNT in PCL films increased the polymer strength, while fractions of 0.03% and more significantly decreased the polymer strength and extensibility compared to the undoped polymer. The PHCH polymeric films showed a similar behavior with an extremum at 0.02% concentration for strength at break.

Phenotypic characteristics of novel swine-origin influenza A/California/07/2009 (H1N1) virus.

BACKGROUND: The 2009 novel A(H1N1) virus appears to be of swine origin. This strain causing the current outbreaks is a new virus that has not been seen previously either in humans or animals. We have previously reported that viruses causing pandemics or large outbreaks were able to grow at a temperature above the normal physiological range (temperature resistance, non-ts phenotype), were found to be inhibitor resistant and restricted in replication at suboptimal temperature (sensitivity to grow at low temperature, non-ca phenotype). In this study, we performed phenotypic analysis of novel A(H1N1) virus to evaluate its pandemic potential and its suitability for use in developing a live attenuated influenza vaccine. OBJECTIVES: The goal of this study is to identify phenotypic properties of novel A(H1N1) influenza virus. METHODS: A/California/07/2009 (H1N1) swine-origin influenza virus was studied in comparison with some influenza A viruses isolated in different years with respect to their ability to grow at non-permissive temperatures. We also analyzed its sensitivity to gamma-inhibitors of animal sera and its ability to agglutinate chicken, human and guinea pig erythrocytes. RESULTS: Swine-origin A/California/07/2009 (H1N1) virus was found to be non-ts and inhibitor resistant and was not able to grow at 25 degrees C (non-ca). We did not find any difference in the ability of the hemagglutinin of A/California/07/2009 (H1N1) virus to bind to erythrocytes of different origin. CONCLUSION: The novel swine-origin A(H1N1) virus displays a phenotype typical of the past pandemic and epidemic viruses. This finding suggests that this virus might be a good wild type parental prototype for live vaccine for potential use for controlling pandemic influenza.